300 kA铝电解槽电、磁、流多物理场耦合仿真
铝电解槽 电磁流场 数值模拟 耦合计算
2009/11/16
将标量电位法和磁标量位法相结合,开发了铝电解槽电场、磁场耦合计算模块,并导出了电磁力场以计算磁流体三维湍流流场及其界面波高. 计算结果表明,垂直磁场基本呈现为反对称关系,水平电流对磁流体运动有显著影响,铝液流场形态基本对称,呈现为4个较大漩涡,铝液界面向中部隆起. 将计算结果与测试值进行了比较,表明该方法能够有效用于铝电解槽生产和设计的物理场仿真计算分析.
CaF2与NdCl3对镁电解物理化学性质的影响
镁 熔盐 物理化学性质
2009/11/16
测定了CaF2与NdCl3对镁电解质18%MgCl2-25%CaCl2-37%NaCl-20%KCl物理化学性质(初晶温度、电导率及密度、表面张力)的影响. 实验结果表明,添加CaF2显著增加了熔盐表面张力,一定程度增加了熔盐的初晶温度和密度,但在添加量小于4%时变化不大,已能满足电解工艺对电解质密度的要求. 添加NdCl3对电解质的密度和初晶温度有一定影响,但添加量小于5%时影响很小,而对表面张...
An Analysis of Contemporary Copper Recycling in China
copper scrap copper recycling self-support ratio
2009/11/16
Copper consumption increased very quickly in China in recent years, which could not be met by inland copper industry. In order to achieve a sustainable development of copper industry, an analysis of c...
EDTA络合高钛渣熔盐反应产物中的Fe3+及TiO2的制备
高钛渣 熔盐法 EDTA
2009/11/16
研究了酸性介质中EDTA对高钛渣与NaOH熔盐反应水洗产物中Fe3+的络合作用,考察了EDTA加入量、反应时间、pH值和温度对Ti4+和Fe3+溶出率的影响. 结果表明,增加EDTA量、延长反应时间、减小pH值及升高温度,Fe3+溶出率增大. 将反应后的固相在105℃下水解可制得球状锐钛型TiO2,平均粒径为100 nm,纯度可达99.3%.
实验测定了1435℃温度下C和N在Fe-C-N和Fe-C-V-N熔体中的饱和溶解度. Fe-C-V熔体中C的饱和溶解度计算式为XC=0.2043+0.8365XV或-lnXC-9.683XC=-11.96XV-0.3916. C和N在Fe-C-V-N熔体中的饱和溶解度随V浓度增加而增加. 根据Fe-C熔体的热力学性质、Fe-C-N熔体中C和N之间的活度相互作用系数、C在Fe-C-V熔体中及C和N在...
HCl-NaCl浸出铅锑合金氧化吹炼渣过程中锑的浸出动力学
铅锑合金 氧化吹炼渣 盐酸
2009/11/16
用液-固多相反应的收缩未反应核模型研究了在HCl-NaCl浸出铅锑合金氧化吹炼渣过程中锑的浸出动力学. 详细考察了浸出温度、盐酸浓度、颗粒粒度对锑的反应速率的影响. 研究结果表明,从铅锑合金氧化吹炼渣中浸出锑过程的控制步骤为固膜扩散,表观反应级数为0.2775. 在实验选取的温度范围内,反应的表观活化能为7.656 kJ/mol. 根据研究结果,建立了浸出锑的宏观动力学方程.
...
KOH亚熔盐法分解钛铁矿
钛铁矿 亚熔盐法 KOH
2009/11/16
以KOH亚熔盐为反应介质,研究了KOH浓度、反应温度与时间、搅拌速率和碱/矿比等因素对钛铁矿在KOH亚熔盐体系中分解率的影响. 结果表明,反应温度、反应时间及KOH浓度为主要影响因素,提高反应温度及KOH浓度均有利于钛铁矿在KOH亚熔盐中的分解,但当反应温度超过260℃时,钛铁矿的分解率又随反应温度的升高而降低;在KOH浓度80%(w)、搅拌速度700 r/min、反应温度260℃、碱/矿质量比5...
La(III) Transport in Dispersion Supported Liquid Membrane Including PC-88A as the Carrier and HCl Solution as the Stripping Solution
liquid separation
2009/11/16
The transport of La(III) through a dispersion supported liquid membrane with polyvinylidene fluoride membrane as the liquid membrane support and dispersion solution including HCl solution as the strip...
Leaching Gold Using Oxidation Products of Elemental Sulfur in Ca(OH)2 Solution Under Oxygen Pressure
gold leaching alkaline solution oxygen pressure
2009/11/16
A gold leaching process by using in situ oxidation products of added elemental sulfur in Ca(OH)2 solution was investigated. A gold concentrate containing 45 g/t Au was tested and 85%~87% of gold were ...
MnO2添加剂对镍铁尖晶石基惰性阳极耐腐蚀性的影响
镍铁尖晶石 惰性阳极 抗腐蚀性
2009/11/16
以氧化物NiO和Fe2O3为原料,添加氧化物MnO2,采用高温固相烧结法制备了NiFe2O4基惰性阳极材料,采用失重法测量了阳极试样的静态热腐蚀速率,并对其腐蚀机理进行了初步探讨. 实验结果表明,添加2%(ω) MnO2粉末的惰性阳极试样的静态热腐蚀速率最低. 由于掺杂的MnO2在晶界处富集,熔盐对晶粒的腐蚀首先在晶界处发生反应生成Mn2AlO4相,而Mn2AlO4相结构致密,冰晶石熔盐通过该相向...
NaOH亚熔盐法处理拜尔法赤泥的铝硅行为
拜耳法 赤泥 氧化铝 铝
2009/11/16
针对拜尔法赤泥铝/硅比偏高的问题,对NaOH亚熔盐法处理拜耳法赤泥过程中的Al, Si行为进行了研究. 考察了溶出温度、碱/泥比、添加CaO等主要因素对终赤泥化学成分和物相结构的影响. 结果表明,溶出温度高、碱/泥比大有利于Al2O3的回收,相应的终赤泥的铝/硅比较低. 在碱/泥比6、溶出温度230℃、时间2 h的条件下,氧化铝回收率可达79.22%,终赤泥的铝/硅比可降到0.39,终赤泥中的硅主...
Na和铝电解质对振动成型TiB2惰性阴极的渗透
振动成型TiB2阴极 Na,铝电解质 渗透
2009/11/16
采用振动成型的TiB2和石墨分别作为Na和铝电解质渗透实验的阴极材料,在工业铝电解条件下电解5 h,考察了Na和铝电解质对其腐蚀渗透情况. XRD分析结果表明,振动成型TiB2阴极的基体中未发现Na或F的单质及化合物,而在石墨阴极中则有NaF和Na3AlF6等物质存在. SEM及EDS分析结果表明,Na, F, Al等元素渗透到TiB2阴极基体中的量极少,渗透到石墨中的量则较多. 可见振动成型Ti...
从含砷硫化铜精矿浸出液中萃取除铁是后续制备砷酸铜的一道工序,P204可从硫酸介质中选择性地萃取铁离子. 实验结果表明,当有机相组成中P204为30%(j),相比1:1, pH"1时,通过三级萃取,铁的萃取率达93%以上,铜和砷几乎不被萃取,萃余液中残铁含量降至9 mg/L以下.
PbS的FeCl3体系发电浸出过程探索
发电过程 浸出 硫化铅
2009/11/13
将化学发电原理应用于人工合成PbS的FeCl3浸出过程. 采用双电池技术及依文思图研究影响发电浸出的各种因素. 结果表明,发电浸出过程在浸出产物的同时还可获得一定的电能,发电浸出体系的内阻是功率输出的关键要素;温度影响发电浸出过程,PbS的FeCl3体系发电浸出过程表观活化能为18.26 kJ/mol;FeCl3和NaCl的浓度以一定的规律影响发电浸出过程.